Product Details
Place of Origin: Shanghai, China
Brand Name: TANKII
Model Number: C35300
Payment & Shipping Terms
Minimum Order Quantity: 1000 KG
Price: negotiable
Packaging Details: Wooned Case
Delivery Time: 7-20 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 500 Tons per month
Model NO.: |
C35300 |
Standard: |
ASTM,DIN,En,GB,JIS |
Transport Package: |
Wooden Case |
Trademark: |
TANKII |
HS Code: |
740921000 |
Origin: |
China |
Production Capacity: |
500tons/Month |
Model NO.: |
C35300 |
Standard: |
ASTM,DIN,En,GB,JIS |
Transport Package: |
Wooden Case |
Trademark: |
TANKII |
HS Code: |
740921000 |
Origin: |
China |
Production Capacity: |
500tons/Month |
C35300
CHEMICAL COMPOSITION
Cu% | Pb% | Fe% | Zn% | |
Nominal Composition | Rem | |||
Min | 60.0 | 1.5 | ||
Max | 63.0 | 2.5 | 0.15 |
PHYSICAL PROPERTIES
Density g/cm3 | 8.47 |
Conductivity at 20°C IACS% | 26 |
Elastic Modulus GPa | 103.4 |
Poisson's ratio | 0.37 |
Thermal expansion coefficient 10-6/ K | 11.3 |
Based on the information provided, it seems you are inquiring about the C35300 strip material. C35300 is a type of brass alloy that is widely used in various industries due to its desirable properties.
Some key characteristics of C35300 brass strip include:
Composition: C35300 is a leaded brass alloy, containing approximately 65% copper, 3% lead, and the remainder primarily zinc.
Mechanical Properties: C35300 has good tensile strength, hardness, and machinability. It is relatively easy to form and fabricate into various components.
Applications: C35300 brass strip is commonly used for items such as hardware fittings, automotive parts, electrical connectors, and other applications where a combination of strength, corrosion resistance, and ease of machining is required.
Availability: C35300 brass strip is commercially available in a range of thicknesses, widths, and tempers to suit different manufacturing and application needs.
If you have any specific questions about the properties, availability, or applications of C35300 brass strip, please feel free to ask, and I'll be happy to provide more detailed information.
MECHANICAL PROPERTIES
State | Diameter | Yield strength | Tensile strength | Elongation | Hardness |
Mpa | MPa | % | HV | ||
O | 10-40 | - | ≥280 | ≥20 | |
1/4H | 10-40 | - | ≥345 | ≥10 | |
1/2H | 10-40 | - | ≥380 | ≥10 |
FABRICATION PROPERTIES
Technique | suitability |
Soldering | Excellent |
Brazing | Good |
Oxyacetylene Welding | Not Recommended |
Gas Shielded Arc Welding | Not Recommended |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Not Recommended |
Seam Weld | Not Recommended |
Butt Weld | Fair |
Capacity for Being Cold Worked | Fair |
Capacity for Being Hot Formed | Poor |
Machinability Rating | 90 |
Alloy System |
designation |
UNS |
EN |
JIS |
GB (China) |
Cu | TK11000 | C11000 | Cu-ETP | C1100 | T2 |
CuCr/Zr |
TK15100 | C15100 | CuZr0.1 | C1510 | TZr0.1 |
TK18160 | C18160 | CuCr0.5Zr | — | ||
TK18150 | C18150 | CuCr1Zr | — | TCr1-0.15 | |
CuCrSiTi | TK18070 | C18070 | CuCrSiTi |
— |
TCr0.3-0.2- 0.05 |
CuNiSnCrTi | TK18090 | — | — | — | |
CuNiP | TK19000 | C19000 | CuNi1P | — | |
CuTi | TK19920 | C19920 | — | — | — |
CuFe |
TK19210 | C19210 | CuFe0.1P | C1921 | TFe0.1 |
TK19400 | C19400 | CuFe2P | C1940 | TFe2.5 | |
CuNiSi |
TK19005 | C19005 | — | — | — |
TK19010 | C19010 | CuNiSi | — | — | |
TK70260 | C70260 | CuNi2Si | C7026 | BSi2-0.45 | |
TK70250 | C70250 | CuNi3SiMg | C7025 | BSi3.2-0.7 | |
TK70250HS | C70250 | CuNi4SiMg | C7025 | — | |
CuNiCoSi | TK70318 | C70318 | CuNi3CoSi | — | — |
Special Brass |
TK42300 | C42300 | CuZn10Sn1NiSi | — | — |
TK42500 | C42500 | CuSn3Zn9 | — | HSn88-2 | |
CuSn / Bronze
|
TK14415 | C14415 | CuSn0.15 | — | TSn0.12 |
TK51000 | C51000 | CuSn5 | C5102 | QSn5-0.2 | |
TK51100* | C51100 | CuSn4 | C5111 | QSn4-0.3 | |
TK51900* | C51900 | CuSn6 | C5191 | QSn6-0.2 | |
TK52100* | C52100 | CuSn8 | C5210 | QSn8-0.3 |