Product Details
Place of Origin: Shanghai, China
Brand Name: TANKII
Certification: ISO9001 SGS
Model Number: C51000
Payment & Shipping Terms
Minimum Order Quantity: 500 KG
Price: negotiable
Packaging Details: Wooned Case
Delivery Time: 7-20 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 300 Tons per month
Material: |
Copper Tin Alloy |
Surface: |
Bright |
Thickness: |
0.05mm-20.0mm |
Width: |
1200mm |
Density: |
8.85 G/cm3 |
Conductivity: |
26 % IACS |
Thermal Expansion Coefficient: |
11.3 10-6/ K |
Material: |
Copper Tin Alloy |
Surface: |
Bright |
Thickness: |
0.05mm-20.0mm |
Width: |
1200mm |
Density: |
8.85 G/cm3 |
Conductivity: |
26 % IACS |
Thermal Expansion Coefficient: |
11.3 10-6/ K |
CHEMICAL COMPOSITION
Sn% | P% | Cu% | |
Nominal Composition | Bal. | ||
Min | 4.2 | 0.03 | |
Max | 5.8 | 0.35 |
PHYSICAL PROPERTIES
Density g/cm3 | 8.85 |
Conductivity at 20°C %IACS | 18 |
Elastic Modulus GPa | 120 |
Poisson's ratio | 0.33 |
Thermal expansion coefficient 10-6/ K | 17.8 |
MECHANICAL PROPERTIES
State | Yield strength | Tensile strength | Elongation | Hardness |
Mpa | MPa | A50% | HV | |
R400 | ≥325 | 400-505 | ≥20 | 125-170 |
R470 | ≥420 | 470-545 | ≥10 | 145-185 |
R525 | ≥510 | 525-625 | ≥9 | 170-210 |
R605 | ≥585 | 605-710 | ≥2 | 180-220 |
R655 | ≥636 | 655-760 | ≥1 | 210-250 |
R690 | ≥675 | 690-785 | ≥1 | 220-270 |
Bending performance
Bending thickness: ≤0.5 mm, bending width: 10 mm
State | 90° R/T | 180° R/T | ||
GW | BW | GW | BW | |
R400 | 0 | 0.5 | 0 | 1.5 |
R470 | 0 | 1 | 0.5 | 1 |
R525 | 0 | 1.5 | 1 | 2 |
R605 | 1 | 2 | 1.5 | 3 |
R655 | 1 | 2.5 | 2 | 4 |
R690 | - | - | - |
Alloy System |
designation |
UNS |
EN |
JIS |
GB (China) |
Cu | TK11000 | C11000 | Cu-ETP | C1100 | T2 |
CuCr/Zr |
TK15100 | C15100 | CuZr0.1 | C1510 | TZr0.1 |
TK18160 | C18160 | CuCr0.5Zr | — | ||
TK18150 | C18150 | CuCr1Zr | — | TCr1-0.15 | |
CuCrSiTi | TK18070 | C18070 | CuCrSiTi |
— |
TCr0.3-0.2- 0.05 |
CuNiSnCrTi | TK18090 | — | — | — | |
CuNiP | TK19000 | C19000 | CuNi1P | — | |
CuTi | TK19920 | C19920 | — | — | — |
CuFe |
TK19210 | C19210 | CuFe0.1P | C1921 | TFe0.1 |
TK19400 | C19400 | CuFe2P | C1940 | TFe2.5 | |
CuNiSi |
TK19005 | C19005 | — | — | — |
TK19010 | C19010 | CuNiSi | — | — | |
TK70260 | C70260 | CuNi2Si | C7026 | BSi2-0.45 | |
TK70250 | C70250 | CuNi3SiMg | C7025 | BSi3.2-0.7 | |
TK70250HS | C70250 | CuNi4SiMg | C7025 | — | |
CuNiCoSi | TK70318 | C70318 | CuNi3CoSi | — | — |
Special Brass |
TK42300 | C42300 | CuZn10Sn1NiSi | — | — |
TK42500 | C42500 | CuSn3Zn9 | — | HSn88-2 | |
CuSn / Bronze
|
TK14415 | C14415 | CuSn0.15 | — | TSn0.12 |
TK51000 | C51000 | CuSn5 | C5102 | QSn5-0.2 | |
TK51100* | C51100 | CuSn4 | C5111 | QSn4-0.3 | |
TK51900* | C51900 | CuSn6 | C5191 | QSn6-0.2 | |
TK52100* | C52100 | CuSn8 | C5210 | QSn8-0.3 |
Mechanical Properties:
Corrosion Resistance:
Wear Resistance:
Bearing Materials: Frequently used in bearings and bushings due to its low friction properties.
Gears and Pulleys: Suitable for manufacturing gears, pulleys, and other components that experience wear.
Marine Applications: Utilized in marine hardware and fittings due to its corrosion resistance.
C51000 can be processed through various methods, including casting, forging, and machining. It can be easily formed and welded, making it adaptable for different manufacturing processes.