Product Details
Place of Origin: Shanghai
Brand Name: TANKII
Certification: ISO9001
Model Number: Cr14Al4
Payment & Shipping Terms
Minimum Order Quantity: 30kg
Packaging Details: waterproof film, weave bag, wooden case
Delivery Time: 8-20 days
Payment Terms: L/C, D/A, D/P, T/T, Western Union,paypal
Supply Ability: 200+ton+month
Surface Treatment: |
Polished |
Technique: |
Cold Rolled |
Application: |
Resistor |
Shape: |
Strip/ Sheet/ Tape |
Appearance: |
Shining, Silver Grey |
HS Code: |
72209000 |
Surface Treatment: |
Polished |
Technique: |
Cold Rolled |
Application: |
Resistor |
Shape: |
Strip/ Sheet/ Tape |
Appearance: |
Shining, Silver Grey |
HS Code: |
72209000 |
Iron Chromium Aluminium Alloys/strip
Nominal Analysis
14.00 Cr, 4.00 Al, Bal. Fe
Max contineous working temperature: 950º C.
Melting Temperature: 1450º C
Electrical Resistivity: 1.25 ohm mm2/m
Has been used extensively as heating elements in industrial furnaces and electrical kilns.
Has less hot strength than Tophet alloys but much higher melting point.
Shanghai TANKII ALLOY MATERIAL CO., LTD.
ALCHROME ALLOY PRODUCER IN CHINA
Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy | ||||||||
Properties Grade | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical Composition (%) |
Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max Continuous Service Temperature(oC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resisivity 20oC (Ωmm2/m) | 1.25 ±0.08 |
1.42 ±0.06 |
1.42 ±0.07 |
1.35 ±0.07 |
1.23 ±0.07 |
1.45 ±0.07 |
1.53 ±0.07 |
|
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal Conductivity | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
(KJ/m@h@oC) | ||||||||
Coefficient of Thermal Expansion(α×10-6/oC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Approximate Melting Point( oC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile Strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Section Variation | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Shrink Rate (%) | ||||||||
Repeatedly Bend Frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous Service Time | no | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic Structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic Property | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |