Product Details:
|
| Certificate: | ISO 9001 | Shape: | Wire |
|---|---|---|---|
| Delivery: | Depends On The Quantity | Condition: | Soft |
| Application: | Resistance Wire | Material: | Iron Chrome Aluminum |
| Color: | Black | ||
| High Light: | nichrome resistance wire,nickel alloys |
||
Industrial Furnace Fecral Electric Resistance Heating Wire Industrial Furnace for Electric Resistance Heating Wire
1.Product Description
Model Number:Resistance heating 0Cr25AL5 wire
Application:Home appliances,industrial furnaces,making electric heating element
Shape:Wire,strip,ribbon etc
Material:Iron-Chromium-Aluminium Alloy
Chemical Composition:Ferro Chrome Aluminium
Ferro Chrome Aluminium:Resistance heating 0Cr25AL5 wire
Standard:AISI,ASTM,DIN,GB etc
Standard:GB/ASTM/AISI/ASME/JIS/DIN etc
Type:Wire /strip /ribbon etc
Certificate:ISO 9001&ROHS&TUV
Conductor Material:Ferro Chrome Aluminium alloy
Surface:Bright and smooth
Surface Treatment:Polished and oxidation
Property:Resistance heating 0Cr25AL5 wire
Feature:Good form stability
Main grades and properties
Grades Properties |
1Cr13Al4 |
0Cr25Al5 |
0Cr21Al6 |
0Cr23Al5 |
0Cr21Al4 |
0Cr21Al6Nb |
0Cr27Al7Mo2 |
|
Chemical composition % |
Cr |
12.0-15.0 |
23.0-26.0 |
19.0-22.0 |
22.5-24.5 |
18.0-21.0 |
21.0-23.0 |
26.5-27.8 |
Al |
4.0-6.0 |
4.5-6.5 |
5.0-7.0 |
4.2-5.0 |
3.0-4.2 |
5.0-7.0 |
6.0-7.0 |
|
Fe |
Balance |
Balance |
Balance |
Balance |
Balance |
Balance |
Balance |
|
Other |
Nb 0.5 |
Mo1.8-2.2 |
||||||
Highest service temperature °C |
950 |
1250 |
1250 |
1250 |
1100 |
1350 |
1400 |
|
ResistivityμΩ.M,20°C |
1.25 |
1.42 |
1.42 |
1.35 |
1.23 |
1.45 |
1.53 |
|
Density (g/cm3 ) |
7.4 |
7.10 |
7.16 |
7.25 |
7.35 |
7.10 |
7.10 |
|
Thermal conductivity KJ/m.H.°C |
52.7 |
46.1 |
63.2 |
60.2 |
46.9 |
46.1 |
45.2 |
|
Coefficient of linear extensibility Α×10-6/°C |
15.4 |
16.0 |
14.7 |
15.0 |
13.5 |
16.0 |
16.0 |
|
Melting point °C |
1450 |
1500 |
1500 |
1500 |
1500 |
1510 |
1520 |
|
Tensile Mpa |
580-680 |
630-780 |
630-780 |
630-780 |
600-700 |
650-800 |
680-830 |
|
Elongation % |
>16 |
>12 |
>12 |
>12 |
>12 |
>12 |
>10 |
|
Reduction % |
65-75 |
60-75 |
65-75 |
65-75 |
65-75 |
65-75 |
65-75 |
|
Hardness H.B. |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
|
Microstructure |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
|