Product Details:
|
| Dia: | 0.1~8mm | Package: | Bobbin, Spools, Wooden Box |
|---|---|---|---|
| Leading Time: | 7~20 Dyas After Getting The Payment | Item: | FeCrAl Wire 0Cr21Al6 0Cr21Al4 0Cr25Al5 Bare Wire 1.0mm With Bright Surface Used For Heating Furnace |
| High Light: | nichrome resistance wire,high resistance wire |
||
FeCrAl Wire 0Cr21Al6 0Cr21Al4 0Cr25Al5 Bare Wire 1.0mm With Bright Surface Used For Heating Furnace
1. Description
FECRAL Has been used extensively as heating elements in industrial furnaces and electrical kilns.
FECRAL Has less hot strength than Tophet alloys but much higher melting point.
Shanghai TANKII ALLOY MATERIAL Co., Ltd.
FECRAL AND ALCHROME ALLOY PRODUCER IN China, MOST PROFESSIONAL IN THE WORLD
We also produce below grades:
Alkrothal 14, Alloy 750, Alferon 902, Alchrome 750, Resistohm 125, Aluchrom, 750 Alloy, Stablohm 750
Kanthal A1, Kanthal, Alloy 875, Resistohm 145, Aluchrom 0, Alchrome 875, MWS-875, Stablohm 875, KAF Kanthal AF, Resistohm Y, Aluchrom Y, Alloy 837, AF KAPM KAPM, Alloy 875 PM, Kanthal APM
Kanthal D, Kanthal, Alloy 815, Alchrome DK, Alferon 901, Resistohm 135, Aluchrom S, Stablohm 812
2.Specification
1).Locomotive resistance strip:
Thickness:0.6mm-1.5mm
Width:60mm-90mm
2).Electric ceramic cooktop resistance strip:
Thickness:0.04mm-1.0mm
Width:5mm-12mm
Thickness&Width:(0.04mm-1.0mm)×12mm(above)
3).Low resistance ribbon:
Thickness&Width:(0.2mm-1.5mm)*5mm
4).Industrial furnace ribbon:
Thickness:1.5mm-3.0mm
Width:10mm-30mm
5).Wire: Diameter:0.1mm-8mm
3. Details of tankii products
| Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy |
||||||||
| Properties Grade |
1Cr13Al4 |
0Cr25Al5 |
0Cr21Al6 |
0Cr23Al5 |
0Cr21Al4 |
0Cr21Al6Nb |
0Cr27Al7Mo2 |
|
| Main Chemical Composition (%) |
Cr |
12.0-15.0 |
23.0-26.0 |
19.0-22.0 |
22.5-24.5 |
18.0-21.0 |
21.0-23.0 |
26.5-27.8 |
| Al |
4.0-6.0 |
4.5-6.5 |
5.0-7.0 |
4.2-5.0 |
3.0-4.2 |
5.0-7.0 |
6.0-7.0 |
|
| Re |
opportune |
opportune |
opportune |
opportune |
opportune |
opportune |
opportune |
|
| Fe |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
Bal. |
|
| Nb0.5 |
Mo1.8-2.2 |
|||||||
| Max Continuous Service Temperature(oC) |
950 |
1250 |
1250 |
1250 |
1100 |
1350 |
1400 |
|
| Resisivity 20oC (Ωmm2/m) |
1.25 ±0.08 |
1.42 ±0.06 |
1.42 ±0.07 |
1.35 ±0.07 |
1.23 ±0.07 |
1.45 ±0.07 |
1.53 ±0.07 |
|
| Density(g/cm3) |
7.4 |
7.1 |
7.16 |
7.25 |
7.35 |
7.1 |
7.1 |
|
| Thermal Conductivity |
52.7 |
46.1 |
63.2 |
60.2 |
46.9 |
46.1 |
45.2 |
|
| (KJ/m@h@oC) |
||||||||
| Coefficient of Thermal Expansion(α×10-6/oC) |
15.4 |
16 |
14.7 |
15 |
13.5 |
16 |
16 |
|
| Approximate Melting Point( oC) |
1450 |
1500 |
1500 |
1500 |
1500 |
1510 |
1520 |
|
| Tensile Strength(N/mm2) |
580-680 |
630-780 |
630-780 |
630-780 |
600-700 |
650-800 |
680-830 |
|
| Elongation(%) |
>16 |
>12 |
>12 |
>12 |
>12 |
>12 |
>10 |
|
| Section Variation |
65-75 |
60-75 |
65-75 |
65-75 |
65-75 |
65-75 |
65-75 |
|
| Shrink Rate (%) |
||||||||
| Repeatedly Bend Frequency(F/R) |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
|
| Hardness (H.B.) |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
|
| Continuous Service Time |
no |
≥80/1300 |
≥80/1300 |
≥80/1300 |
≥80/1250 |
≥50/1350 |
≥50/1350 |
|
| Micrographic Structure |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
Ferrite |
|
| Magnetic Property |
Magnetic |
Magnetic |
Magnetic |
Magnetic |
Magnetic |
Magnetic |
Magnetic | |
Typical application areas of FeCrAl wires
Pre-heating of aluminium
Homogenising of aluminium
Heat treatment in the metallurgical industry
Drying of ore concentrates
Drying of materials in the wood processing industry
Roasting and drying in the food industry
Baking in large bakery ovens
Drying of chemicals
Drying and stoving of paints (stoving furnaces)
Please call me at +86-18017475212 or email to me for more information on FeCrAl products.