Stainless Thermal Spray Wire 2Cr13 (SS420) 1.2mm/1.6mm/2.0mm
TANKII 420 stainless steel wire, specifically designed for arc spray processes. 420 SS forms a dense, well bonded coating, with excellent wear resistance and good corrosion resistance. It is widely used for machine elements repair, dimensional restoration, and wear resistant application. 420 SS's low shrink rate characteristics allows for increased coating thickness on parts requiring heavier coatings.
SS 420 is stainless steel wire, specifically designed for arc spray processes.SS 420 forms a dense, well bonded
coating, with excellent wear resistance and good corrosion resistance. It is widely used for machine elements repair, dimensional restoration, and wear resistant application. SS 420 low shrink rate characteristics, allows for increased coating thickness on parts requiring heavier coatings. It can equivalent to: Tafa 60T, Sulzer Metco Metcoloy 2.
Chemical Composition, %
Cr | Si | Mn | C | Fe |
13.0 | 1.0 | 1.0 | 0.3 | Bal |
Mechanical Properties
Coating Hardness | HRC 40-45 |
Bonding Strength | 48.95 N/mm2 |
Deposit Rate | 10 lbs/hr/100A |
Service Temperature | Up to 550C 1022F |
Condition | Solid Wire |
Diameter | 1.6mm(14 ga),2.0mm,3.175mm |
Package Size | 10kg,15kg,or up to client's demand |
TYPICALDEPOSIT SURFACEPREPARATION:
•TypicalHardness HRC40-45
•BondStrength 6500psi
•DepositRate 10lbs /hr/100A
•DepositEfficiency 70% cleaning.
•WireCoverage 0.8oz/spft2/mil
•SurfaceTexture *Variable
•CorrosionResistance Good
STANDARDSIZES&PACKAGING:
Diameter | Dimension | Packing | Wire Weight |
Tolerance | |||
1/16"(1.6mm) | +0/-0.05 | D 300 Spool | 15kgs(33 lbs)/spool |
2.0mm | +0/-0.05 | D 300 Spool | 15kgs(33 lbs)/spool |
1/8"(3.17mm) | +0/-0.05 | Coil Form | 20-400kgs/coil |