Product Details
Place of Origin: China
Brand Name: Tankii
Certification: ISO 9001
Model Number: 0Cr25Al5
Payment & Shipping Terms
Minimum Order Quantity: 50kg
Packaging Details: spool,coil
Delivery Time: 5-30 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 2000kg/month
Application: |
Heating,Industry,furnace Heating Wire |
Shape: |
Strip,wire |
Material: |
Iron-Chromium-Aluminium Alloy |
Chemical Composition: |
Fe Cr Al |
Dimensions: |
0.05-12mm |
Surface: |
Acid White/oxidized |
Size: |
Customzied |
Certificate: |
ISO 9001 |
Application: |
Heating,Industry,furnace Heating Wire |
Shape: |
Strip,wire |
Material: |
Iron-Chromium-Aluminium Alloy |
Chemical Composition: |
Fe Cr Al |
Dimensions: |
0.05-12mm |
Surface: |
Acid White/oxidized |
Size: |
Customzied |
Certificate: |
ISO 9001 |
0Cr25Al5 Oxidized Surface Electrictrical Resistance Heating Alloys FeCrAl Wire Used In Furnace
Product Description
Tankii 0Cr25Al5 is one kind of normal material of Fe-Cr-Al alloy.
FeCrAl alloy has the characteristic of high resistivity,low temperature resistance coefficient,high operating temperature,good anti-oxidation and anti-corrosion under high temperature.
It is widely used in industrial furnace, household appliances, industry furnace, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.
Size dimension range:
Wire: 0.01-10mm
Ribbons: 0.05*0.2-2.0*6.0mm
Strip: 0.05*5.0-5.0*250mm
Bar:10-50mm
FeCrAl alloy series: OCr15Al5,1Cr13Al4, 0Cr21Al4, 0Cr21Al6, 0Cr23Al5, 0Cr25Al5, 0Cr21Al6Nb,0Cr27Al7Mo2, and etc.
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | -- | |
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
continuous service time(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |