Product Details
Place of Origin: Shanghai, China
Brand Name: TANKII
Certification: ISO9001 SGS
Model Number: NiCr 90/10
Payment & Shipping Terms
Minimum Order Quantity: 20KG
Price: negotiable
Packaging Details: Spool + Carton + Wooned Case
Delivery Time: 7-20 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 100 Tons per month
Material: |
Nickel-chrome Alloy Wire |
Diameter: |
0.02-8.00mm |
Sample: |
Accepted Small Order |
Spool: |
DIN 63-DIN250 |
Resiitivity: |
70.6 |
Material: |
Nickel-chrome Alloy Wire |
Diameter: |
0.02-8.00mm |
Sample: |
Accepted Small Order |
Spool: |
DIN 63-DIN250 |
Resiitivity: |
70.6 |
fast delivery Chromel ni90cr10 n90 wire nichrome 90 heating wire for vape
Nickel-chromium, nickel, ferrochrome alloy wire with electric high temperature oxidation resistance, high strength, not soften and a series of advantages.
When used in a long time, the same type and the permanent elongation is very small, with excellent comprehensive properties, is to produce high-quality varieties of choice for electric components.
Cr10Ni90 is an ideal material, it has good ductility,workability and weldability under high temperature and seismic strength.
Nickel-chromium alloy with high and stable resistance, corrosion resistance, surface oxidation resistance, excellent coil-forming ability.
|
Performance/
material
|
Cr10Ni90
|
Cr20Ni80
|
Cr30Ni70
|
Cr15Ni60
|
Cr20Ni35
|
Cr20Ni30
|
|
|
Composition
|
Ni
|
90
|
Rest
|
Rest
|
55.0-61.0
|
34.0-37.0
|
30.3-34.0
|
|
Cr
|
10
|
20.0-23.0
|
28.0-31.0
|
15.0-18.0
|
18.0-21.0
|
18.0-21.0
|
|
|
Fe
|
--
|
≤1.0
|
≤1.0
|
Rest
|
Rest
|
Rest
|
|
| Max. continuous service temp. of element(ºC) | 1200 | 1200 | 1250 | 1150 | 1100 | 1100 | |
|
Melting Point
|
1400
|
1400
|
1380
|
1390
|
1390
|
1390 |
|
|
Resistivity
|
0.706+-0.05
|
1.09+-0.05
|
1.18+-0.05
|
1.12+-0.05
|
1.00+-0.05
|
1.04+-0.05
|
|
|
Density(g/cm3)
|
8.7
|
8.4
|
8.1
|
8.2
|
7.9
|
7.9
|
|
|
Elongation at rupture
|
≥20
|
≥20
|
≥20
|
≥20
|
≥20
|
≥20
|
|
| T.S.(MPa) | ≥490 | ≥600 | ≥600 | ≥600 | ≥600 | ≥600 | |