Product Details
Place of Origin: Shanghai
Brand Name: TANKII
Certification: ASTM/GB
Model Number: 1Cr13Al4,fecral125
Payment & Shipping Terms
Minimum Order Quantity: 20kg
Price: negotiable
Packaging Details: wires in spool, and packed in boxes,then on wooden pallet
Delivery Time: 7-15 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 200+ton+per month
Surface: |
Bright, Annealed, Soft, Smooth |
Resistivity: |
1.25 |
Density: |
7.4 |
Surface: |
Bright, Annealed, Soft, Smooth |
Resistivity: |
1.25 |
Density: |
7.4 |
| Alloy Type / Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
|
Composition |
Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re |
Opportune
|
|||||||
| Fe |
Rest
|
|||||||
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(℃) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20℃(μm.m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m.h.℃) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | -- | |
| Coefficient of lines expansion(ax10-6/℃) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.(℃) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Elongation at rupture(%) | ＞16 | ＞12 | ＞12 | ＞12 | ＞12 | ＞12 | ＞10 | |
| Repeat Bending frequency(F/R) | ＞5 | ＞5 | ＞5 | ＞5 | ＞5 | ＞5 | ＞5 | |
| Continuous servicetime(Hours/℃) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥80/1350 | ≥80/1350 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 650-800 | |
| Variation of area(％) | 65-75 | 60-75 | 60-75 | 60-75 | 60-75 | 60-75 | 60-75 | |
| Micrographic Structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic Properties | Magnetic | Magnetic |
Magnetic
|
Magnetic | Magnetic | Magnetic | Magnetic | |