Product Details
Place of Origin: China
Brand Name: TANKII
Certification: ISO9001
Model Number: 0Cr27Al7Mo2/
Payment & Shipping Terms
Minimum Order Quantity: 20kg
Price: negotiation
Packaging Details: On Spool,In Coil
Delivery Time: 5-10 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 20, 000kg/month
Application: |
Industry |
Shape: |
Rod/bar/round Material |
Material: |
FeCrAl |
Chemical Composition: |
Ferro Chrome Aluminium |
Surface: |
Bright,acid White/oxidized |
Application: |
Industry |
Shape: |
Rod/bar/round Material |
Material: |
FeCrAl |
Chemical Composition: |
Ferro Chrome Aluminium |
Surface: |
Bright,acid White/oxidized |
FeCrAl( 0Cr27Al7Mo2) resistance alloy
With the characteristics of high resistance, low coefficient of electric resistance, high operating temperature, good corrosion resistance under high temperature, it is widely used in the single crystal furnace, sintering furnace, ceramic calcining furnace and heat treatment furnace.
0Cr27Al7Mo2
Chemical Content(%)
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other | ||
Max | |||||||||||
0.05 | 0.025 | 0.025 | 0.20 | Max 0.40 | 26.5~27.8 | Max 0.60 | 5.0~7.0 | Bal. | Mo 1.8-2.2 |
Mechanical Properties
Max Continuous Service Temp | 1350ºC |
Resisivity at 20ºC | 1.45 ohm mm2/m |
Density | 7.1 g/cm3 |
Thermal Conductivity | 46.1 KJ/m·h·ºC |
Coefficient of Thermal Expansion | 16.0×10-6/ºC |
Melting Point | 1510ºC |
Tensile Strength | 637~784 Mpa |
Elongation | Min 12% |
Section Variation Shrink Rate | 65~75% |
Repeatedly Bend Frequency | Min 5 times |
Continuous Service Time | - |
Hardness | 200-260HB |
Micrographic Structure | Ferrite |
Magnetic Property | Magnetic |
Temperature Factor of Electrical Resistivity
20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC |
1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 |