Honeycomb Substrates 0.05mm Thickness FeCrAl Strip Coil

Product Details

Place of Origin: Shanghai, China

Brand Name: TANKII

Certification: ISO9001:2008

Model Number: 0Cr21Al6Nb

Payment & Shipping Terms

Minimum Order Quantity: 20kg

Price: Negotiation

Packaging Details: Spool, carton, plywod case with plastic film as clients required

Delivery Time: 7-20 DAYS

Payment Terms: L/C, T/T, Western Union, Paypal

Supply Ability: 300+TON+MONTH

Get Best Price
Contact Now
Specifications
Highlight:

0.05mm FeCrAl Strip Coil

,

Honeycomb Substrates FeCrAl Strip Coil

,

Corrosion Resistance FeCrAl Strip Coil

Thickness:
0.02-0.15mm
Application:
Metallic Honeycomb Substrates, Heating Elements, Glass Top Hob
Composition:
Iron, Chromium, Aluminium
Color:
Silver Grey
Size:
As Clients' Requirement
Shipment:
By,sea, By Express, By Air
Thickness:
0.02-0.15mm
Application:
Metallic Honeycomb Substrates, Heating Elements, Glass Top Hob
Composition:
Iron, Chromium, Aluminium
Color:
Silver Grey
Size:
As Clients' Requirement
Shipment:
By,sea, By Express, By Air
Description
Honeycomb Substrates 0.05mm Thickness FeCrAl Strip Coil

FeCrAl Alloy Foil/ Strip Coil 0.05mm Thickness for Metallic Honeycomb Substrates
 

 

The high aluminum content, in combination with the high chromium content causes the scaling temperature to increase up to 1425 C (2600F ); Under the headline heat resistance, these FeCrAl alloys are compared with commonly used Fe and Ni base alloys. As can be seen from that table, the FeCrAl alloys have superior properties as compared to the other alloys in most environments.

It should be noted that, during alternating temperature conditions, the yttrium addition to the AF alloy which also is known as the Fecralloys alloys, improves the adherence of the protecting oxide, making the service life of components in the AF alloy longer than that of the A-1 grade.

Fe-Cr-Al alloy wires are made of iron chromium aluminum base alloys containing small amounts of reactive elements such as yttrium and zirconium and produced by smelting, steel rolling, forging, annealing, drawing, surface treatment, resistance control test, etc.
Fe-Cr-Al wire was shaped by means of high speed automatic cooling machine of which the power capacity is controlled by computer, they are available as wire and ribbon(strip).

 

Features and advantages
1. High using temperature, the maximum using temperature can reach 1400C (0Cr21A16Nb, 0Cr27A17Mo2, etc.)
2. Low temperature coefficient of resistance
3. Lower thermal expansion coefficient than the Ni-base super-alloys.
4. High electrical resistivity
5. Good corrosion resistance under high temperature, especially under the atmosphere containing sulfides
6. High surface load
7. Creep-resistant
8. Lower raw-material cost, Lower density and cheaper price compared with Nichrome wire.
9. Superior oxidation resistance at 800-1300ºC
10. Long service life

The formation of metastable alumina phases due to the oxidation of commercial FeCrAl alloy wires (0.5 mm thickness) at various temperatures and time periods has been examined. Samples were isothermally oxidised in air using a thermogravimetric analyzer (TGA). The morphology of the oxidised samples was analyzed using an Electronic Scanning Electron Microscope (ESEM) and X-ray on the surface analysis was done using an Energy Dispersive X-Ray (EDX) analyzer. The technique of X-Ray Diffraction (XRD) was used to characterize the phase of the oxide growth. The entire study showed that it was possible to grow high-surface area gamma alumina on the FeCrAl alloy wire surfaces when isothermally oxidised above 800°C over several hours.

 

 


Iron Chrome Aluminum
 

OCr25Al5

CrAl25-5
 
23.0

71.0
 
6.0
 

OCr20Al5

CrAl20-5
 
20.0

75.0
 
5.0
 

OCr27Al7Mo2
   
27.0

65.0

0.5

7.0

0.5

OCr21Al6Nb
   
21.0

72.0

0.5

6.0

0.5

 


Iron Chrome Aluminum
   

OCr25Al5

Can be used in operating conditions up to 1350°C, although can become embrittled.

Heating elements of high temperature furnaces and radiant heaters.

OCr20Al5

A ferromagnetic alloy which can be used at temperatures up to 1300°C. Should be operated in dry surroundings to avoid corrosion. Can become embrittled at high temperatures.

Heating elements of high temperature furnaces and radiant heaters.